Poly Naphthalene Formaldehyde Condensate(PNS)

Product Description

High Range Water-Reducing Admixture

Poly Naphthalene Sulfonate Formaldehyde Condensate Concrete Admixture

Description
PNS is a high range water reducer, commonly referred to as a superplasticizer. It is an aqueous solution of a modified naphthalene sulfonate and organic compounds. PNS is made of naphthalene, sulfonic acid, HCHO and Alkali through sulphuration, hydrolyzation, condensation and neutralization reaction. PNS contains no added chloride. PNS meets the requirements of chemical admixture specifications for concrete: GB8076-1997, GB50119-2003.

Uses
PNS produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps.
PNS is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation. UNF-5 will also fluidize concrete, making it ideal for tremie concreting or other applications where high slumps are desired.
Compatible with Portland cement, normal Portland cement, Portland slag cement, fly-ash cement and Portland pozzolanic cement etc.

Advantages
Produce high performance concrete of C80 with slump of 50mm-70mm or C60 with slump of 180mm-200mm.
Slump control at the job site without adding water.
Higher early and ultimate strengths. Given the same amount of cement and slump requirement, this product can increase the concrete stress by 40-110%, 40-90%, 30-80% and 30-50% on day 1, 3, 7, and 28 respectively.
Improves concrete placebility with no loss in strength.
At addition rate of 0.5% -1.0%, PNS can save cement 12%-20% in comparison to the concrete at the same slump and strength.
Higher strengths may be achieved more economically.
Improves cohesiveness and reduces concrete segregation.
Concrete achieves higher durability.
PNS has wide application. It does not retard and introduce air. It will reduce the chemical heat in the cement and produces concrete with lower permeability.
Properties, Features & Characteristics

Appearance: Light brown powder. Non-poisonous, odorless, non-flammable and non-corrosive to steel bars.
Remarkable Plasticity: As a condition of blending where amount of cement and collapsibility are fixed aforehand, mixing water can be decreased by 10-30% when it is admixed with reinforced concrete at 0.3-1.5%.
Improve miscibility of concrete amalgamator with water and collapsibility as well. As a condition of equivalent blending, collapsibility can be increased by 12cm when it is added at standard blend dosage.
Parameters & Acceptance Criteria(Sodium salt of polynaphthalene sulfonic acid)
Parameters Criteria Actual results

Solid Content 92% min 93.41%
Moisture, % <= 8.0 7.1
Fineness 5.0% max 1.04%
pH value 7 - 9 7.8
Sodium Sulfate Content 18.0% max 16.71%
Chlorides Content 2.0% max 0.21%
Surface Tension 68-72 Mn/m 70
Cement Flowing Rate 230mm min 240mm
Concrete Reducing Water Rate 18% min 20.00%
Steel-bar Corrosion None None

Addition Rates
PNS can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%.

Direction
Prepare solutions as required.
Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%).
The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds.
Package, Storage & Handling
For powder: Woven fabric bag with plastic liner. Net weight: 25kg +/- 0.13 kg.