H1060 Epoxy Primer (2K)

Product Description

H1060 Epoxy Primer (2K)
Composing:
It is a kind of two component protective primer that is made from diversiform modified resin, rustproofing pigment, shield fillers, hollow microsphere, organic solvent, etc. with H1160 hardener according to the proportion of 4:1.  
 
Characteristics:
This primer has excellent adhesive force. It can fast dry at normal temperature; it has good capacity of elasticity and extension to deformation generated by the temperature change of substrate, good mechanical character, and excellent salt spray resistance and strong anticorrosive property. Therefore, it is a kind of high-performance automobile primer.

Field of Application:
This product is applied to metal products that have the higher requirement to anticorrosive property, anticorrosive coatings of car body, car frame, car box and car bridge of luxurious cars, as well as the primer of electrolytic plate, galvanized plate, aluminium alloy and other nonferrous metal products and glass fiber reinforced plastic.

Main technical standard:
 Item  Technical Index  Inspection Standard
Index of Original Primer  Outward appearance  No foreign matter and obvious granule, easy to homogenize  Visual measurement
 Color & appearance  Olivine or sage green thick liquid  Visual measurement
 Involatile constituent (120 Degree centigrade /1h)  ≥60 %  GB/T6751
 Fineness  ≤35μm  GB/T1724
H1160Original Hardener  Outward appearance  Light yellow transparent liquid  Visual measurement
 Amine value  135~165 mg KOH/g  0.1NHCl titration
Film CoatingPerformance Index  Color & appearance  Olivine or sage green, leveling and smoothness  Visual measurement
 Dry time  ≤6h (Hard dry in 25 Degree centigrade)  GB/T1728
   ≤0.5h (Baking dry in 80 Degree centigrade)  
 Adhesive force  Grade 1  GB/T9286
 Pliability  ≤1 mm  GB/T1731
 Impact strength  ≥50 kg. cm  GB/T1732
 Burnishing performance (20 times)  Easy to Burnishing, not adhibit sandpaper  GB/T1770
 Nitrocellulose lacquer resistance  Not lift, not bleed red  Visual measurement
 Water resistance (168h)  Not bubble, not rust  GB/T5209
 Salt water resistance (264h)  Not bubble, not peel off  GB/T 1763
 Heat and humidity resistance (96h)  Grade 1  GB/T 1765
 Salt spray resistance (216h)  Grade 1  GB/T 1765

Reference for construction and notes:
1.It is suitable for spray coating and brush coating. Implement the rust removing treatment to substrate before construction (spray sand to grade Sa2.5, surface roughness 30~70μm).

2.Mix well H1060 epoxy primer and H1160 hardener according to the proportion of 4:1, keep curing for 20min (room temperature), use H1260 thinner to dilute for 18~20s (T-4, 25 Degree centigrade), wet-to-wet spray painting twice, dry for 6 hours (or 0.5H/80 Degree centigrade). After drying, scrape putty or spray intermediate primer and finishing paint.

3.Mix paint every time according to construction using amount, the paint that has mixed into hardener should be used up in time (use for 4 h at normal temperature), or it will be discarded due to becoming thicker.

4.The storage life is one year from the date of commencement of production (if it is beyond the storage life, please confirm according to the standard inspection; if it is still qualified, it can be continuously used).

Packing and Storage:
Packing Specification: Primer is packed 4L printing iron drums. Hardener is packed 1L printing iron drums.
Storage Condition: 5-35 degree centigrade, store in a cool, dry well-ventilated place.