Silicone for glassfiber bushing and wire
(SDA-166T)
Product application:

SDA-166T fire performance fiberglass bushing, electrical wire silicon resin is a new circumstance -protected organic silicon material with the character of anti-ultraviolet, heat resisting, pliability, transparence and flameout automatically. It is widely used to manufacture the fiberglass bushing and silicon rubber wire because of its strong mechanical strength and flameout automatically film after curing.
Technical parameter:

Appearance: Transparent or translucent liquid.
Density (25degree, g/cm3) 0.9-1.0
Viscosity (25degree, MPa. S) 2000-5000
Diluent: (you can choose to use) toluene and xylene
Film characteristic (e. G. ): (test method as JIS-C-2122)
Resistor (normal stage. CM) 10
Dielectric strength (normal stageKV/0.1mm) 5.0
Heating loss (250degree, 72hrs, %) < 1.0
Bendability (250degree, above100hrs) all right
Solvent resistance(toluene, xylene, 5mins) no change
Painting pipe characteristic (e. G. ): (Test method as JB/T709*3-1993)

Resin adhesion amount (g/m) 1.65 3.32
Automatically flameout time (close alcohol lamp flame directly 5mins) 2~3 4~7
Breakdown voltage (BDV, KV) 3~4 6~10
Temperature resistant -30~300

Using direction:

1. Suggestion: Confect concentration: 10~30%
2. Curing agent: 2% of base solution
3. Curing condition: 130~2000C 3~10min

Packing and shipment:

200KG iron drum packing or as per customer's request. (you can choose to use with different produce process. )
Don't contact the fire, avoid drench and insolate between the shipments
Storage life: 6 months at 25C in the airtight machine (can be used if the product is valid by test over 6 months)