Extrusion Antirust 5A06 Aluminum Alloy

1.Chemical composition ( mass fraction ) ( % )
Fe≤ 0.08, Zn≤ 0.2, Si≤ 0.05, Cu≤ 0.1,  Mn 0.5-0.7, Mg 5.8-6.2, Ti 0.02-0.05, Be 0.0002-0.005,  Al margin
2.Characteristic 
5A06 Aluminum is Al~Mg antirust aluminum alloy, has high strength and corrosion stability,is widely used in Marine applications such as ships, cars, aircraft components, metro light rail, the need for stringent fire prevention of the pressure vessel (such as liquid tanker, refrigerated trucks, refrigerated container), cooling device, television tower, drilling equipment, transportation equipment, missile component and armor.
3.Hot treatment specification
1).homogenizing annealing: heat 460~475ºC; heat preservation 12h~14h;  air cooling.
2).rapid annealing: heat 310~350ºC; heat preservation 30~120min; air or water cooling.
3).high temperature anniling: heat 310~335ºC; when finished product thickness ≥6mm or <6mm, heat preservation 30~180min or 30~120min; air cooling.
4).low temperature anniling: heat 250~300ºC or 150~180ºC; heat preservation 1~2h or 2~3h; air cooling.