Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Ceramic Fiber Cloth;
Al2O3+Sio2: 98%;
Bulk Density: 500kg/M3~550kg/M3;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Funnel, Sleeve, Round and Square Tube, Spider,etc;
Material: Flint Clay , Bauxite ,Andalusite ,Mullite;
Bulk Density: 2100-2350 Kg/M3;
Cold Crushing Strength: 30 - 40 MPa;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Feature: Instant Materials;
Type: Refractory Material;
Shape: Plate;
Material: Silicon Carbide (SiC);
Size: 35mm-400mm;
Ppi: 10/20/30;
Application: Grey Iron, Ductile Iron, Copper, Brass;
Common Size 1: 40X40X15mm 50X50X15mm 50X50X22mm;
Common Size 2: 50X75X22mm 75X75X22mm 75X100X22mm;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: MGO;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 18-19%;
Bulk Density: 2.95g/cm3;
Cold Crushing Strength: 45-60MPa;
Thermal Shock Under Load: 1600;
MGO: 75-84%;
Al2O3: 8-14%;
Fe2o3: 0-5.0%;
|