| Specification |
CAS No.: 24937-78-8;
Bonding Function: Cryogenic Adhesive;
Morphology: Solid-State;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing;
Material: EVA;
Classification: Hot Melt;
Main Agent Composition: EVA;
Promoter Composition: Resin;
Color: Colorful;
Other Names: Color Glue Stick;
Models Name: Colorful Hotmelt Glue Sticks;
MOQ: 1000kg;
Main Raw Material: EVA, Resin;
Brand: Gzww;
Type: Hotmelt Glue Sticks;
Packing: Export Carton;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|