| Specification |
Classification: Semi-Silica;
Feature: Instant Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
C: 6~7;
Al2O3: 65~75;
Bulk Density: 2.8~3.15;
CCS: 70~130;
Type: Heat-Resistant Material;
Material: Alumina Block;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Ladle Refractories Sliding Gate Plates for Steel M;
Al2O3: 80% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Ladle Refractories Sliding Gate Plates for Steel M;
Al2O3: 80% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Ladle Refractories Sliding Gate Plates for Steel M;
Al2O3: 80% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Ladle Refractories Sliding Gate Plates for Steel M;
Al2O3: 80% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|