| Specification |
Material: Alumina Block;
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
|
Application: Blast Furnace, Cement Kiln, Ceramic Kiln, Chemical Kiln, Glass Kiln, Steel-Making Furnace;
Material: Light Weight Silica-Alumina;
Refractoriness (℃): 1580< Refractoriness< 1770;
Testing Laboratory: Support;
Al2O3: 58%;
Sio2: 40%;
Cao+MGO: 0.00%;
|
Application: Blast Furnace, Cement Kiln, Ceramic Kiln, Chemical Kiln, Glass Kiln, Steel-Making Furnace, Industrial Furnaces;
Material: Sio2 94-96%;
Refractoriness (℃): 1580< Refractoriness< 1770;
Product Name: Silica Fire Brick;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Standard Size: 230X114X65 or Custom Size;
Feature: Long Time Materials, Hot Sale, Instant Materials;
Type: Refractory Material;
Shape: Brick;
|
Application: Blast Furnace, Cement Kiln, Glass Kiln, Steel-Making Furnace, Industrial Furnace;
Material: Light Weight Silica-Alumina;
Refractoriness (℃): 1770< Refractoriness< 2000;
Product Name: Refractory Chamotte Bricks;
Weight of Brick: 3-4kg/Pices;
Bulk Density g/cm3: 2.00-2.35;
Keyword: Low Creep Fire Clay Brick;
Cold Crushing Strength MPa: More Than 25;
Permanent Linear Change: More Than1100;
Refractoriness°c: More Than1700;
Color: Yellow Fire Brick;
|
Application: Blast Furnace, Cement Kiln, Ceramic Kiln, Chemical Kiln, Glass Kiln, Steel-Making Furnace, High Temperature Furnace;
Material: High Alumina;
Refractoriness (℃): 1770< Refractoriness< 2000;
Product Name: Fireclay Brick;
Weight of Brick: 3-4kg/Pices;
Bulk Density g/cm3: 2.00-2.35;
Keyword: Refractory Fire Brick;
Cold Crushing Strength MPa: More Than 25;
Permanent Linear Change: More Than1100;
Refractoriness°c: More Than1700;
Color: Yellow Fire Brick;
|