| Specification |
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 100 Cycle;
Rul: 1700ºC;
CCS MPa: 60;
MGO: 85-87;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
|
Product Name: Magnesia Chrome Bricks;
Apparent Porosity: 17-18%;
Refractoriness Under Load: 1600c;
Cold Crushing Strength: 50-55 MPa;
Fe2o3: 4-6.5%;
Magnesia Chrome Bricksfeature: Good Thermal Shock Resistance;
Applications: Cement Rotary Kiln, Glass Kiln Regener;
Brick Material: Magnesium Oxide (MGO) and Chromium Oxide;
Al2O3 Content (%): 3.8-4.2%;
MGO Content (%): 65-80%;
Cao Content (%): 0.2-0.4%;
Cro Content (%): 7-17%;
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesite, Periclase and Spinel;
|
Application: Cement Industry, Chemical Industry, Coking Industry, Glass Industry, Steelmaking Industry, High Temperature Kiln;
Content: 90% Magnesia Brick;
Performance: Magnesia Chrome Refractory Bricks;
Production Process: Sintered Magnesia Brick;
Softening Temperature: ≥1650℃;
Product Name: Magnesia Chrome Bricks;
Apparent Porosity: 17-18%;
Refractoriness Under Load: 1600c;
Cold Crushing Strength: 50-55 MPa;
Fe2o3: 4-6.5%;
Magnesia Chrome Bricksfeature: Good Thermal Shock Resistance;
Applications: Cement Rotary Kiln, Glass Kiln Regener;
Brick Material: Magnesium Oxide (MGO) and Chromium Oxide;
Al2O3 Content (%): 3.8-4.2%;
MGO Content (%): 65-80%;
Cao Content (%): 0.2-0.4%;
Cro Content (%): 7-17%;
Refractoriness: 1770< Refractoriness< 2000;
Feature: High Temperature Resistance;
Type: Refractory Material;
|
Product Name: Magnesia Chrome Bricks;
Apparent Porosity: 17-18%;
Refractoriness Under Load: 1600c;
Cold Crushing Strength: 50-55 MPa;
Fe2o3: 4-6.5%;
Magnesia Chrome Bricksfeature: Good Thermal Shock Resistance;
Applications: Cement Rotary Kiln, Glass Kiln Regener;
Brick Material: Magnesium Oxide (MGO) and Chromium Oxide;
Al2O3 Content (%): 3.8-4.2%;
MGO Content (%): 65-80%;
Cao Content (%): 0.2-0.4%;
Cro Content (%): 7-17%;
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesite, Periclase and Spinel;
|
Product Name: Magnesia Chrome Bricks;
Apparent Porosity: 17-18%;
Refractoriness Under Load: 1600c;
Cold Crushing Strength: 50-55 MPa;
Fe2o3: 4-6.5%;
Magnesia Chrome Bricksfeature: Good Thermal Shock Resistance;
Applications: Cement Rotary Kiln, Glass Kiln Regener;
Brick Material: Magnesium Oxide (MGO) and Chromium Oxide;
Al2O3 Content (%): 3.8-4.2%;
MGO Content (%): 65-80%;
Cao Content (%): 0.2-0.4%;
Cro Content (%): 7-17%;
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesite, Periclase and Spinel;
|