Spring flat bar
Material: 60Si2Mn 50CrVA, 55CrMnA, 60Si2CrA, 51CrV4
Standard: GB/T702-2008
| Width |
50 |
60 |
70 |
80 |
90 |
100 |
120 |
130 |
150 |
160 |
180 |
| Thickness |
6-13 |
6-25 |
6-35 |
6-35 |
6-40 |
7-45 |
8-50 |
8-40 |
8-30 |
10-30 |
12-27 |
Our Steel Mill Is Founded in 1993, Located at Handan, Hebei.
Our mill can produce high quality Spring Steels, Flat Steel Bars, Leaf Springs, which are widely used in automobile industry.
Warmly welcome Client from all over the world to visit our mill, we can provide most competitive price.
1.Description
Spring steel refers to steel due to the elasticity in the quenched and tempered condition, and specifically for the manufacture of springs and elastic components. Spring steel depends on its ability to elastically deform, i.e., within the prescribed range, the ability to withstand a certain elastic deformation so that the load does not occur in the permanent deformation after the load is removed.
Back to Top
2.Application
Spring steel flat bars are widely used on auto fittings, auto manufacturing, hardware tools, chain manufacturing and other machinery manufacturing industry. Automobile plate spring
Back to Top
3.Size Ranges
Width: 40mm-150mm; Thickness: 4mm-60mm
Back to Top
4.All Grades Comparison
| GB |
ASTM |
JIS |
ISO |
DIN |
BS |
ANFR |
GOST |
| 65# |
1065 |
/ |
TypeDC,SC |
CK67 |
060A67 |
XC65 |
65 |
| 70# |
1070 |
/ |
TypeDC,SC |
/ |
070A72 |
XC70 |
70 |
| 85# |
1086 |
SUP3 |
TypeDC,SC |
CK85 |
060A86 |
XC85 |
85 |
| 65Mn |
1066 |
/ |
/ |
/ |
080A67 |
/ |
65Γ |
| 60Si2Mn |
9260 |
SUP6,SUP7 |
61SiCr7 |
60SiCr7 |
Z51A60 |
60Si7 |
60C2 |
| 60Si2CrA |
9254 |
SUP12 |
55SiCr63 |
/ |
/ |
/ |
60C2XA |
| 55CrMnA |
5155 |
SUP9 |
55Cr3 |
55Cr3 |
525A58 |
55Cr3 |
/ |
| 60CrMnBA |
51B60 |
SUP11A |
60CrB3 |
/ |
/ |
/ |
55XΓP |
| 60CrMnMoA |
4161 |
SUP13A |
60CrMo33 |
60CrMo4 |
705A60 |
/ |
/ |
| 50CrVA |
6150 |
SUP10A |
51CrV4 |
50CrV4 |
735A51 |
51CrV4 |
50CrΦA |
Back to Top
5.Quality Standard
GB/T 1222 Spring Steels
JIS G 4801 Spring Steels
EN 10089 Hot rolled steels for quenched and tempered springs
Back to Top
6.Chemical Composition(%)
| Steel Grade |
C |
Mn |
Si |
P |
S |
Cr |
Ni |
B |
Cu |
Mo |
V |
| 65# |
0.62-0.70 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
| 70# |
0.62-0.75 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
| 85# |
0.82-0.90 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
| 65Mn |
0.62-0.70 |
0.90-1.20 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
| 60Si2Mn |
0.56-0.64 |
0.70-1.00 |
1.50-2.00 |
0.035 max |
0.035 max |
0.35 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
| 60Si2CrA |
0.56-0.64 |
0.40-0.70 |
1.40-1.80 |
0.025 max |
0.025 max |
0.70-1.00 |
0.25 max |
/ |
0.25 max |
/ |
/ |
| 55CrMnA |
0.52-0.60 |
0.65-0.95 |
0.17-0.37 |
0.025 max |
0.025 max |
0.65-0.95 |
0.35 max |
/ |
0.25 max |
/ |
/ |
| 60CrMnBA |
0.56-0.64 |
0.70-1.00 |
0.17-0.37 |
0.025 max |
0.025 max |
0.70-1.00 |
0.35 max |
0.0005-0.0040 |
0.25 max |
/ |
/ |
| 60CrMnMoA |
0.56-0.64 |
0.70-1.00 |
0.17-0.37 |
0.025 max |
0.025 max |
0.70-0.90 |
0.35 max |
/ |
0.25 max |
0.25-0.35 |
/ |
| 50CrVA |
0.46-0.54 |
0.50-0.80 |
0.17-0.37 |
0.025 max |
0.025 max |
0.80-1.10 |
0.35 max |
/ |
0.25 max |
/ |
0.10-0.20 |
Back to Top
7.Mechanical Properties(Quenched and Tempered Condition)(T=20°C if not differently stated)
| Steel Grade |
Tensile Strength Rm (Mpa) |
Yield Strength Rp0.2 (Mpa) |
Elongation A5 (%) |
Area Reduction Ratio C (%) |
| 65# |
980 min |
785 min |
9 min |
35 min |
| 70# |
1030 min |
835 min |
8 min |
30 min |
| 85# |
1130 min |
980 min |
6 min |
30 min |
| 65Mn |
980 min |
785 min |
8 min |
30 min |
| 60Si2Mn |
1275 min |
1180 min |
5 min |
25 min |
| 60Si2CrA |
1765 min |
1570 min |
6 min |
20 min |
| 55CrMnA |
1225 min |
1080 min |
9 min |
20 min |
| 60CrMnBA |
1225 min |
1080 min |
9 min |
20 min |
| 50CrVA/td> |
1275 min |
1130 min |
10 min |
40 min |
Back to Top
8.Heat Treatment
| Steel Grade |
Quenching Temperature (°C) ( |
Media |
Tempering Temperature (°C) |
| 65# |
840 |
oil |
500 |
| 70# |
830 |
oil |
480 |
| 85# |
820 |
oil |
480 |
| 65Mn |
830 |
oil |
540 |
| 60Si2Mn |
870 |
oil |
480 |
| 60Si2CrA |
870 |
oil |
420 |
| 55CrMnA |
830-860 |
oil |
460-510 |
| 60CrMnBA |
830-860 |
oil |
460-520 |
| 50CrVA |
850 |
oil |
500 |