Specification |
Shape: Brick;
Sic: 65%~90%;
Bulk Density: ≥2.3G/Cm3;
|
Classification: Carbon-Ceramic Composites;
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance;
Shape: Plate;
Usage: High-Temperature Furnaces;
Bulk Density: >=2.75g/cm3;
Max Service Temp: 1550c;
Compressive Strength: >=1300 Kg/Cm2;
Thermal Conductivity at 1000ºC: 13.5-14.5kcal/M.Hr.C;
Modulus of Rupture at Room Temp: >=500kg/Cm2;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Shape: Brick, Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Shape: Brick, Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Shape: Brick, Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|