Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Fusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Zro2: 31%~41%;
Al2O3: ≥45%;
Sio2: ≤15%;
Bulk Density: ≥3.7g/cm3;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Used: Refractory Stone, Castable, Nozzle Material;
Color: Brown;
Mohs: 9;
Customized: OEM/ODM;
Trues Density: 3.9g/cm3;
Melting Temperture: 2050;
Fe2o3(Max): 0.3%;
Al2O3 (Min): 95%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Used: Refractory Stone, Castable, Nozzle Material;
Color: Brown;
Mohs: 9;
Customized: OEM/ODM;
Trues Density: 3.9g/cm3;
Melting Temperture: 2050;
Fe2o3(Max): 0.3%;
Al2O3 (Min): 95%;
|
Refractoriness (℃): Refractoriness> 2000;
Shape: Grit;
Advantage: 20 Years' Manufacturer,QC and Lead Time Guaranteed;
Al2O3: 95% Min;
Fe2o3: 0.3% Max;
Sio2: 1.2% Max;
TiO2: 3.0% Max;
Cao: 0.4% Max;
MGO: 0.4% Max;
Magnetic Particles: 0.05% Max;
Hardness: 9 Mohs;
Specific Gravity: 3.8 g/cm3 Min;
Application: Refractory Bricks;
Sample: Yes, Provide as Request;
Certificates: ISO9001/ISO14001/ISO18001;
|
Refractoriness (℃): Refractoriness> 2000;
Shape: Grit;
Advantage: Manufacturer, Can Be Customized;
Al2O3: 95% Min;
Fe2o3: 0.3% Max;
Sio2: 1.2% Max;
TiO2: 3.0% Max;
Cao: 0.4%;
MGO: 0.4%;
Magnetic Particles: 0.05% Max;
Hardness: 9 Mohs;
Specific Gravity: 3.8 g/cm3 Min;
Application: Refractory Bricks, Castables, Other Materials;
|