Sealants

MS710 High Tack Strength Ultra Crystal MS Polymer Sealant For Structural Bonding

High Tack And Strength Clear MS Hybrid Sealant HM-MS710 Items C*a/T*b/S*c/O*d Unit Typical Value Requirement Test Std. Eqv. Std. Appearance - - Fine, uniform paste without bubbles, crusts, gels Test StQ/QY-00-T001d - Density g/cm3 1.04 1.05±0.02 GB/T 13477.2 - Tack free Properties Uncured min 20 ≤30 GB/T 13477.5 ASTM D2377:2000 Hardness, Shore A Properties Cured - 35 ≥35 GB/T 531.1 ISO 7619-1:2004 Elongation at break Properties Cured % 350 ≥350 GB/T 528 ISO 37:2005 Tensile Strength Properties Cured MPa 2.0 ≥2.0 GB/T 528 ISO 37:2005 These figures are only intended as a guide and should not be used in preparing specifications. PRODUCT DESCRIPTION MS710 is a high bonding strength silane modified polyther MS hybrid polymer sealant. it is made of Howell own technology MS polymer and shows a great bonding performance and high tack to various substrates that require high and initial strength. It is all transparent, low VOC, eco-friendly and paintable, thus an ideal material for bonding parts need good strength and quick fixation.High glossy with various colors. Fully transparent Strong bonding on almost all surfaces High strength and good hardness Superior physical properties One component, easy to process Eco friendly-no isocyanate, solvent, halogen or acid components: harmless to health- Paintable with water based coatings Durable elasticity after curing APPLICATIONS Sealing and bonding of the construction industry applications Sanitary and kitchen application: Mildew proof Structure bonding having the demand of expansion adhesion USAGE Construction: Cut the branch opening, put on the glue nozzle, cut the glue nozzle into a suitable slope, and apply it tothe construction site with a glue extrusion gun. During pneumatic gluing, the air pressure isrecommended not to exceed 0.4 MPa, and the construction temperature is recommended to be 4°C -40°C Curing: Place the glued parts in the air. After the skin is formed, it will cure from the surface to the inside. Thecuring depth will be 2~4mm within 24 hours at room temperature and 55% relative humidity. As timegoes by, the curing depth gradually increases. Storage: Unused glue should be tightened immediately and the nozzle should be sealed for storage. When usingit again, if there is a little crust on the seal, just remove it and it will not affect normal use. During thestorage process, a small amount of crusting may also appear on the branch mouth. After removal, it canbe used normally without affecting product performance. PACKAGE Standard 300ml plastic bottle packing, 24pcs/carton; 500-600ml flexible film packing, 20pcs/carton;A variety of packaging options are available to meet your needs. Store the original sealant in a dry place, the temperature should not be higher than 27 °C, and the storageperiod is 12 months from the date of production SAFETY PRECAUTIONS Ensure the product is kept out of children's reach. Always read the product specifications, material details, and instructions on the container packaging before use. Company Profile Nanjing Howell New Materials Technology Co., Ltd. Room 501, Unit 7, Xingzhihui, Xinghuo Rd 19th, Jiangbei New District, Nanjing, (211899), Jiangsu, China. American Warehouse:Add: 1006 CROCKER RD, DOOR E5, WESTLAKE, OH 44145

Hw-606 High Efficiency Anti-Mildew Indoor and Outdoor Antibacterial Glue Glass Aluminum Ceramic Wood Kitchen and Bathroom Sealant

China Factory 2-Component UV-Curing Silicone Sealant Pastebonding Adhesive for Insulating Glass Extruder Machine Production Line

Factory Price Concrete Adhesive Clear Waterproof Firestop Sealant Silicone

KASTAR 115 Low Price Waterproof Windshield PU Sealant

Walls Concrete Cracks Sealant