Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 37%~77%;
Bulk Density: 0.55g/cm3~1.25g/cm3;
Classification Temperature: 1260ºC~1730ºC;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Castable;
Al2O3: 30-90;
Sio2: 15-48;
Size: Customizable;
Application Limit Temp: 1000-1700;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Castable;
Al2O3: 30-90;
Sio2: 15-48;
Size: Customizable;
Application Limit Temp: 1000-1700;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Application: Refractory, Industrial Ceramic;
Type: Ceramic Plates;
Material: Silicon Carbide Ceramic;
Refractoriness Under Load: 1600-1700ºC;
Apparent Porosity: 17%~20%;
Cold Crushing Strength: 80-100MPa;
Sic: 65-90%;
Bulk Density: 2.3-2.6g/cm3;
|