Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: 28%~40%;
Bulk Density: 2.0g/cm3-2.25g/cm3;
Cold Crushing Strength: ≥30MPa;
Refractoriness: ≥1700ºC;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Mullite;
Bulk Density(g/cm3): 0.6g/cm3;
Al2O3: 40%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Bulk Density: 0.6g/cm3~0.8g/cm3;
|