Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 37%~77%;
Bulk Density: 0.55g/cm3~1.25g/cm3;
Classification Temperature: 1260ºC~1730ºC;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Castable;
Al2O3: 30-90;
Sio2: 15-48;
Size: Customizable;
Application Limit Temp: 1000-1700;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Module, Ceramic Fiber Module;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2, Al2O3+Sio2+Zro2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1350/1430;
Certifiacte: ISO9001, CE, etc;
Linear Shrinkage After Heating: 1000ºC*24h<=2.5-3.5;
Bulk Density(g/cm3): 180-240;
Thermal Conductivity: 0.09-0.175;
Al2O3: 34-45%;
Sio2: 50-54%;
Zro2: 15%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Castable;
Al2O3: 30-90;
Sio2: 15-48;
Size: Customizable;
Application Limit Temp: 1000-1700;
|