Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: 47%~72%;
Fe2o3: ≤0.5%;
Bulk Density: ≥2.95g/cm3;
Apparent Porosity: ≤17%;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Application: Refractory, Industrial Ceramic;
Type: Ceramic Plates;
Material: Silicon Carbide Ceramic;
Refractoriness Under Load: 1600-1700ºC;
Apparent Porosity: 17%~20%;
Cold Crushing Strength: 80-100MPa;
Sic: 65-90%;
Bulk Density: 2.3-2.6g/cm3;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430/1600;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1500;
Bulk Density(g/cm3): 64-160;96/128;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.08;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430/1600;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1500;
Bulk Density(g/cm3): 64-160;96/128;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.08;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430/1600;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1500;
Bulk Density(g/cm3): 64-160;96/128;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.08;
|