Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 30~80%;
Apparent Porosity: 20%~26%;
Refractoriness: Sk30, Sk32, Sk34, Sk36, Sk 38, Sk40;
Cold Crushing Strength: 20-70MPa;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|