| Specification |
Classification: Clay;
Feature: Good Mechanical Strength, High-Temperature Resistant, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: ≥40%;
Bulk Density: ≥2.3G/Cm3;
Apparent Porosity: ≤18%;
|
Classification: Silicon Carbide (Sic);
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Raw Material: Alloy;
Bulk Density: 2.7 g/cm3;
Apparent Porosity: 5~18%;
Certifiacte: ISO9001, CE, etc;
Feature 2: High Hardness, High Thermal Shoc;
Application: Steel Industry;
Thermal Shock Resistance: Excellent;
Classification Temperature: 1500-1800 ºC;
Color: Blank, Grey;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Clay;
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 35-80%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Sk32/Sk34/Sk35/Sk36/Sk37/Sk38;
Refractoriness Under Load (0.2MPa): 1350-1700 ºC;
Size Control: Accurate;
Testing Laboratory: Support;
Type: Refractory Material;
Material: Alumina Block;
|
Classification: Clay;
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 35-80%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Sk32/Sk34/Sk35/Sk36/Sk37/Sk38;
Refractoriness Under Load (0.2MPa): 1350-1700 ºC;
Size Control: Accurate;
Testing Laboratory: Support;
Type: Refractory Material;
Material: Alumina Block;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Products Name: Non Swirling Nozzle Tundish Nozzle;
Zirconia Plate: Customzied;
Application 1: Steel Making;
Application 2: Tundish Continuous Casting;
Zirconia Products: Zirconia Ring, Plate, Insert etc;
Zirconia Ring, Plate: Be Assembled to Ladle Sliding Gate Plate;
Function: Flow Control The Steel Molten;
Customizable Shapes and Services: Available;
Cnm/Mnc Tundish Nozzle: Available;
Workmanship: Pressing or Casting;
Upper Nozzle(Stationary Nozzle): Fixed Tundish Nozzle;
Lower Nozzle: Exchangable Tundish Nozzle;
Tundish Well Block: Supplied;
Advantage: Thermal Shock Resistance;
CNC System: Capable;
|