Specification |
Shape: Brick;
Sic+ Si3n4: No Less Than 94%;
Bulk Density: No Less Than 2.65g/cm3;
Cold Compresive Strength: at Least 150 MPa;
|
Classification: Silicon Carbide;
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (Sic);
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 16-22%;
Cold Crushing Strength: 80-130MPa;
Refractoriness Under Load: 1550-1700;
Fe2o3: 0.3-1.0%;
Sick: 73-90%;
Si3n4: 0-25;
|
Classification: Silicon Carbide;
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (Sic);
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 16-22%;
Cold Crushing Strength: 80-130MPa;
Refractoriness Under Load: 1550-1700;
Fe2o3: 0.3-1.0%;
Sick: 73-90%;
Si3n4: 0-25;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Shape: Brick, Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Shape: Brick, Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|