| Specification |
Type: Graphite Sheets;
Wide: 1-1.5m;
Thickness: 0.3-2mm;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Flake Graphite;
Composition: Expanded Graphite;
|
Application Area: Chemical Industry, Electron Industry, Friction Materials, Heat Conduction;
Feature: Thermal Shock Resistance;
Type: Artificial Graphite;
Tensile Strength: 4.6 MPa;
Compressibility: 43.1%;
Resilient Rate: 10.6%;
Stress Relaxation: 9.7%;
Ash: 0.32%;
Carbon: 98.6%;
Fluorine: 10ppm;
Sulpur: 660ppm;
Chlorine: 20ppm;
Working Temperature: -240~600;
|
Application Area: Chemical Industry, Electron Industry, Friction Materials, Heat Conduction;
Feature: Thermal Shock Resistance;
Type: Artificial Graphite;
Thermal Conductivity(X.Y): 1100~1300W/Mk;
Thermal Conductivity(Z): 10~15W/Mk;
Thermal Diffusivity: 750~850(mm^2/S);
Specific Heat(70cj / Gk): 0.85;
Heat Resistance: 400c;
Tensile Strength(X.Y): 28MPa;
Tensile Strength(Z): 0.4MPa;
Bending Test(R5 / 180c;): >10000;
Bending Test(R2 / 180c;): >5000;
Electric Conductivity: 12000s/Cm;
Flame Retardant Rating: V0;
|
Application Area: Chemical Industry, Electron Industry, Friction Materials, Heat Conduction;
Feature: Thermal Shock Resistance;
Type: Artificial Graphite;
Thermal Conductivity(X.Y): 700~900W/Mk;
Thermal Conductivity(Z): 10~15W/Mk;
Thermal Diffusivity: 500~700(mm^2/S);
Specific Heat(70cj / Gk): 0.85;
Heat Resistance: 400c;
Tensile Strength(X.Y): 20MPa;
Tensile Strength(Z): 0.45MPa;
Bending Test(R5 / 180c;): >10000;
Bending Test(R2 / 180c;): >5000;
Electric Conductivity: 10000s/Cm;
Flame Retardant Rating: V0;
|
Application Area: Chemical Industry, Electron Industry, Friction Materials, Heat Conduction;
Feature: Thermal Shock Resistance;
Type: Artificial Graphite;
Thermal Conductivity(X.Y): 1300~1500W/Mk;
Thermal Conductivity(Z): 10~15W/Mk;
Thermal Diffusivity: 820~900(mm^2/S);
Specific Heat(70cj / Gk): 0.85;
Heat Resistance: 400c;
Tensile Strength(X.Y): 30MPa;
Tensile Strength(Z): 0.12MPa;
Bending Test(R5 / 180c;): >10000;
Bending Test(R2 / 180c;): >5000;
Electric Conductivity: 18000s/Cm;
Flame Retardant Rating: V0;
|