Specification |
Application: Aerospace, Electronics, Medical, Vacuum Brazing;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Insulating Ceramics;
Compressive Strength: 2300MPa;
Coating Thickness: 8-30μm;
Coating Layer: Mo/Mn;
Plated Layer: Nickel/Copper/Gold etc.;
Thermal Conductivity: 25W/(M.K);
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
Density: 3.7g/cm3;
|
Application: Industrial Ceramic;
Type: Ceramic Plates;
Product Name: Alumina Ceramic Foam Filter;
Model No.: Sf-Acf;
Pore Density(Ppi): 10-40;
Porosity(%): 80-90;
Operating Temperature: <1100celsius;
Bending Strength(MPa): >0.6;
Compression Strength(MPa): >0.8;
Thermal Sgock Resistance(Times/1100): 6;
Color: White;
Filter Shape: Square/Round or Custom;
Size: According to Clients Requirements;
Features 1: Effectively Remove The Inclusions;
Features 2: Improve Surface Quality/Product Performance;
Features 3: Improve Microstructure;
Material: Alumina Ceramic;
|
Application: Ceramic Decorations, Refractory, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Plates;
Product Name: Silicon Carbide Ceramic Foam Filter;
Temperature: 1500;
Pore Density (Ppi): 10-50;
Density: 0.36-0.5g/cm3;
Uses: Grey Iron/Ductile Iron/Nonferrous Alloy;
Porosity (%): 80-90;
Operating Temperature: <1500 Degrees Celsius;
Material: Silicon Carbide;
|
Application: Ceramic Decorations, Refractory, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Plates;
Product Name: Silicon Carbide Ceramic Foam Filter;
Uses: Grey Iron/Ductile Iron/Nonferrous Alloy;
Pore Density (Ppi): 10-50;
Porosity (%): 80-90;
Operating Temperature: <1500 Degrees Celsius;
Material: Silicon Carbide;
|
Application: Ceramic Decorations, Refractory, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Plates;
Product Name: Silicon Carbide Ceramic Foam Filter;
Uses: Grey Iron/Ductile Iron/Nonferrous Alloy;
Pore Density (Ppi): 10-50;
Porosity (%): 80-90;
Operating Temperature: <1500 Degrees Celsius;
Material: Silicon Carbide;
|