Specification |
Application: Industrial Ceramic;
Type: Ceramic Balls;
Zro2: >94.8%;
Y2o3: >5.2 %;
Density: 5.95~6.0;
Hv Hardness: >8;
Water Absorption: <0.01;
Wear Loss(G/Kgh): <1.3;
Crushing Strength(3mm): >16000n;
Size: 0.3-30mm;
Sphericity: >95%;
Material: Zirconia Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Piston;
Material: Alumina Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Tube, Ceramic Rods;
Product Name: High Hardness Zirconia Ceramic Tube Pipe Rod;
Color: White, Black, Beige, Blue;
Hardness: 1300-1365 MPa;
Raw Material: Zro2+Y2o3;
Denisty: 6.02 g/cm3;
Design: Round, Square or Special Design;
Surface Finish: Ginding and Polishing;
Features: Excell Wear-Resistance, High Temperature Resistance;
Tempetature: 2300 C;
Grain Size: Less Than 0.5 Um;
Bending Strength: 1150 Gpa;
Forming Process: Hot Pressing;
Usage: Work as Ceramic Rod Shaft, Wear Resistance;
Applications: Refractory, Industrial Ceramic;
Package: Save Packing;
Material: Zirconia Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Rod, Ceramic Rods;
Product Name: High Polishing Zirconia Zro2 Ceramic Rod;
Color: White, Black, Beige, Blue;
Hardness: 1300-1365 MPa;
Raw Material: Zro2+Y2o3;
Denisty: 6.02 g/cm3;
Design: Round, Square or Special Design;
Surface Finish: Ginding and Polishing;
Features: Excell Wear-Resistance, High Temperature Resistance;
Tempetature: 2300 C;
Grain Size: Less Than 0.5 Um;
Bending Strength: 1150 Gpa;
Forming Process: Hot Pressing;
Usage: Work as Ceramic Rod Shaft, Wear Resistance;
Applications: Refractory, Industrial Ceramic;
Package: Save Packing;
Material: Zirconia Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Rods;
Product Name: Polished Zirconia Rod with High Temperature;
Color: White, Black, Beige, Blue;
Hardness: 1300-1365 MPa;
Raw Material: Zro2+Y2o3;
Denisty: 6.02 g/cm3;
Design: Round, Square or Special Design;
Surface Finish: Ginding and Polishing;
Features: Excell Wear-Resistance, High Temperature Resistance;
Tempetature: 2300 C;
Grain Size: Less Than 0.5 Um;
Bending Strength: 1150 Gpa;
Forming Process: Hot Pressing;
Usage: Work as Ceramic Rod Shaft, Wear Resistance;
Applications: Refractory, Industrial Ceramic;
Package: Save Packing;
Material: Zirconia Ceramic;
|