3,679 Diamond Tool Graphite Mould
results from78 suppliers
Carbon Graphite Mold Utilized for Diamond Cutting Cured Concrete Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
High Density Carbon Graphite Molds for Diamond Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Carbon Graphite Mold Utilized for Diamond Cutting Asphalt Blads Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Corrosion Resistant Carbon Graphite Molds for Diamond Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Graphite Mold for Diamond Point Tools, Electroplated Diamond Grit and CBN Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Carbon Graphite Mold Utilized for Diamond Cutting Stone Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Graphite Sinter Mold for Diamond Tools
- Feature: High Density
- Application: Foundry
- Sample: Available
- Material: Molded Graphite, Isostatic Graphite.Ect.
- Grain Size: Below 325 Mesh
- Type: Graphite Mold
Fine-Grain High Purity Graphite Mold for Hot-Pressing Hand Grinder Diamond Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Strong Corrosion Resistant Carbon Graphite Sintered Molds for Diamond Tools
- Type: Graphite Mold
- Carbon Content: High-Carbon
- Forming Way: Molded Graphite
- Crystal Morphology: Compact Crystalline Graphite
- Composition: 99.9% High Purity Graphite
- Grade: High Purity Graphite
Graphite Mold Utilize for Diamond Floor Prep Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Strong Oxidation Resistant Carbon Graphite Sintered Molds for Diamond Tools
- Bulk Density: 1.70-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Carbon Graphite Mold Utilized for Diamond Cutting Combination Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Utilized for Diamond Cutting Brick Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Customizable Long Tool Life Graphite Mold for Concrete Diamond Wire
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Graphite Mold for Diamond Grinding Segment Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Utilized for Diamond Cutting Refractory Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Graphite Molds for Diamond Tools
- Size: Customers' Requested
- Compress Strength: 62MPa
- Application: Melting Metal
- Bending Strength: 40MPa
- Grain Size: 0.8mm/325mesh
- Bulk Density: 1.68g/cm3-1.85g/cm3
Hot-Pressing Graphite Puck, Pad Mould for Concrete Grinding Diamond Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Suitable for Diamond Cutting Cured Concrete Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Suitable for Diamond Cutting Ductile Lrow Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Fine-Grain High Purity Graphite Mould for Manufacture Diamond Tools to Cut and Drill Reinforced and Precast Concrete, Asphalt, Refractories
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mould Used for Diamond Tool Dressing Diamond Wheel
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
High Temperature Stability Carbon Graphite Molds for Diamond Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Compression Resistance Sintering Graphite Mould for Diamond Tool
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Utilized for Diamond Cutting Ring Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Utilized for Diamond Cutting Ductile Lrow Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Carbon Graphite Mold Suitable for Diamond Cutting Block Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
High Purity Carbon Graphite Mould Used for Poltava Diamond Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Carbon Graphite Mold Utilized for Diamond Cutting Green Concrete Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Low Friction/Wear Carbon Graphite Molds for Diamond Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Carbon Graphite Mold Suitable for Diamond Cutting Green Concrete Blades Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
High Strength Graphite Sintering Mold for Diamond Tools
- Product Name: Graphite Sintering Mold for Diamond Tools
- Name: Graphite Sintering Mold
- Density: Above1.82
- Min Order Quanity: 50PCS
- Type: Graphite Mold
- Carbon Content: High-Carbon
Carbon Graphite Mold Utilized for Diamond Wire Tool
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
High Purity Graphite Molds for Diamond Tools
- Size: Customers' Requested
- Compress Strength: 62MPa
- Application: Melting Metal
- Bending Strength: 40MPa
- Grain Size: 0.8mm/325mesh
- Bulk Density: 1.68g/cm3-1.85g/cm3
Custom Design High Purity Graphite Mold for Hot-Pressing Diamond Tools Applications
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Oxidation Resistant Carbon Graphite Molds for Diamond Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
High Purity Graphite Mold for Hot-Pressing Concrete Grinder Diamond Tools
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Factory Customized Graphite Mould for Diamond Tool in Casting Industry
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25
Sintering Graphite Mold Utilize for Diamond Floor Prep Tools
- Bulk Density: 1.80-1.91g/cm3
- Electrical Resistivity: 10-13
- Flexural Strength MPa: More Than 43MPa
- Compressive Strength: More Than 80MPa
- Thermal Conductivity: 85-139.2W/M*K
- Temperature Resistance: No More Than 4350 Degree
Customized Graphite Mold Utlized in Diamond Tools of Floor Polishing
- Density: 1.70-1.92g/cm3
- Resistivity: Less Than 12
- Compressive Strength: More Than 70MPa
- Porosity: Less Than 26%
- Elasticity Modulus : 6-18gpa
- Thermal Expansion Coefficient: 1.47-4.25