Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Material: Alumina Cement;
Thickness: 6-50mm;
Width: 610/1220mm;
Length: 7200mm or Your Requirment;
Chemical Composition: Al2O3+Sio2≥99%;
Ultimate Strength (≥ MPa): 0.08-0.12;
Fiber Diameter: 3-5μm;
Application: Refractory Furnace Lining Insulation Materials;
Density (Kg/M³ ): 128;
Feature 1: Low Thermal Conductivity,Low Heat Storage;
Feature 2: Good Thermal Shock Resistance;
Feature 3: Reasonable Price;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: High Efficency;
Type: Refractory Material;
Shape: Square;
Material: Alumina;
Color: White, Ivory;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-2.95g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Synthetic Material;
Application Area: Preheating Zone/Safety Zone;
Bulk Density: 2.2;
Apparent Porosity%: 16;
Tsr: 16 Cycle;
CCS: 57;
Alkali Resistance: 1st Grade;
Size: Customer Made;
|
Usage: Rto;
Materials: Cordierite/Corundum Mullte/Mullite/Silicon Oxide;
Size: 150*150*100mm, 100*100*150mm etc;
Holes: 25holes, 40holes, 43holes, 50holes, 60holes;
Hole Shape: Round, Square, Hexagonal, Triangular;
Max.Working Tem. (Celsius Degree): 1320-1700;
|