Specification |
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Cold Crushing Strength: ≥40MPa;
Density: ≥2.9 g/cm3;
Apparent Porosity: ≤3%;
C: 10;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Aggregate and Powder;
Material: Bauxite Ore;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Powder and Aggregate;
Material: Alumina Block;
Tensile Strength: 7-13MPa;
Bulk Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory..Others;
Compressive Strength: 4-9MPa;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Aggregate and Powder;
Material: Alumina Cement;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Aggregate and Powder;
Material: Al2O3;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|