Specification |
Usage: Thermal Insulation Coatings, Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Length: 1200mm;
Width: 1000mm;
Min Thickness: 3mm;
Max Thickness: 100mm;
Density: 220kg/M3 -350kg/M3;
Color: White;
Shapes: Can Be Cut to Any Shapes;
Loss of Ignition, Loi, %: <8%;
Types: Inroganic Type and Organic Type;
Shrinkage, %,: <3;
Compressive Strength,: >0.2;
Thermal Conductivity, W/M•K: 0.03-0.18;
Smell: Inorganic Type Has No Smell;
Refractory Grade: Non-Inflammable;
Application: Oven, Furnace, Boiler Heat Insulation Liner;
|
Usage: Filter Material, High Temperature Insulating Material, Thermal Insulation;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Textile;
Kind: Ordinary Ceramic Fiber;
Province: Shandong;
Name: Ceramic Fiber Textiles;
Manufacturer: Luyang;
Product: Aluminum Silicate Textiles;
Raw Material: Aluminum Silicate Fiber;
Material: Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1000ºC;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
Color: White;
Density(Kg/M3): 64, 96, 128, 160 Kg/M3;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Manufacturer: Luyang;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Inorganic Hardened Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: 1260 Ceramic Fiber;
Color: White;
Rupture Strength(MPa): 0.6;
Ignition Lost (at 1000ºCx5hr) Lol%: 8;
|