Specification |
Usage: Thermal Insulation Coatings, Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Width: 610mm/1220mm;
Length: as Your Request;
Density: 96kg/M3, 128kg/M3;
Temperature: 1050c - 1430 C;
Color: White;
Melting Point: 1760c;
Tensile Strength: >30kpa;
Fiber Diameter (Um): 3-5;
Shrinkage (24 Hours ): ≤2.5 (1000°c);
Shot Content (Φ≥0.212mm) (%): <15;
Thermal Conductivity (W/M·K): 0.035-0.18;
Shapes: Any Shape Can Be Cut;
Smell: No Smell;
Inorganic: No Binder;
Refractory Grade: Non-Inflammable;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1100/1300ºC;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Color: White;
Thermal Shock Resistance: Excellent;
Features: High Flexibility,Low Weight,Low Heat Storage, etc.;
Application: for Blanket/Board/Paper/Textiles;
High Temperature Use: Refractory Expansion Joints/Furnace Seals/Packing;
|
Usage: High Temperature Insulating Material, Complex Spaces/Kiln Car Infill/Fire Door Infill;
Temprature Classification: 1260ºC-1430ºC;
Chemical Composition:: SiO2, Al2O3, Zro2,Color,Shot Content;
Shape: Bulk;
Kind: Ordinary Ceramic Fiber;
Customized Size: Yes;
Features: Excellent Chemical Stability/Low Heat Storage etc;
Classlfcation Temperature (P): 1260ºC;
Al2O3: >=43%;
Sio2: >=54%;
Shot Content (%): <=15%;
Fiber Dameter (Pm): 2-4/3-5;
H.S.Code: 68061010;
|
Usage: Filter Material, High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Density (Kg/M³ ): 160;
Thermal Conductivity: 0.09(400c);
Fiber Diameter: 3-5 Um;
Ultimate Strength (≥ MPa): 0.3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃, 1430 ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Double- Needled;
Kind: High Purity Ceramic Fiber;
Item: Ceramic Fiber Blanket;
Temperature: 1050-1430 C;
Density: 64/96/128/160 Kg/M3;
Color: White/ Pure White;
Al203+Sio2: 97-99 %;
Application: Heat Insulation;
Refractory Grade: Non-Inflammable;
Melting Point: 1760 ºC;
Thickness: 6mm-50mm Thickness;
Width: 610mm/1220mm or Customized;
Length: 3600/3660/3810/7200/7620mm or Customized;
Tensile Strength: >30 Kpa;
Type: Heat-Resistant Material;
Thermal Conductivity (W/M·K): 0.035-0.18;
Performance: Excellent;
|