| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Length: 1200mm;
Width: 1000mm;
Min Thickness: 3mm;
Max Thickness: 100mm;
Density: 220kg/M3 -350kg/M3;
Color: White;
Shapes: Can Be Cut to Any Shapes;
Loss of Ignition, Loi, %: <8%;
Types: Inroganic Type and Organic Type;
Shrinkage, %,: <3;
Compressive Strength,: >0.2;
Thermal Conductivity, W/M•K: 0.03-0.18;
Smell: Inorganic Type Has No Smell;
Refractory Grade: Non-Inflammable;
Application: Oven, Furnace, Boiler Heat Insulation Liner;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|