Specification |
Application: Electronics, Industrial;
Standard: JIS, GB, DIN, ASTM;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Surface: Bright;
Treatment: Hydrogen Annealing;
Tensile Strength, Ultimate, Annealed: 827 MPa;
Size: 0.018mm-10.0mm;
Density ( @ 20.0° C/ 68.0° F): 8.10 G/Cm;
Conductor Material: Ni-Cr-Al-Fe;
Resistivity: 1.33±0.07;
Melting Point: 1350° C;
Resistance: 800 Ohm-CIR-Mil/FT or 0.000134 Ohm-Cm;
Composition: Nickel: 75%, Chromium 20%, Aluminium: 2.5%, Copper;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: Nickel Alloy;
Alloy: Alloy;
Type: Nickel Alloy Tube;
Powder: Not Powder;
Wall Thickness: 0.3-3mm;
MOQ(Kg): 50;
Elongation (≥%): 30;
Shape: Tube;
Est. Time(Days): 14;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: Nickel Alloy;
Alloy: Alloy;
Type: Nickel Alloy Tube;
Powder: Not Powder;
Wall Thickness: 0.3-3mm;
MOQ(Kg): 50;
Elongation (≥%): 30;
Shape: Tube;
Est. Time(Days): 14;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: Nickel Alloy;
Alloy: Alloy;
Type: Nickel Alloy Tube;
Powder: Not Powder;
Wall Thickness: 0.3-3mm;
MOQ(Kg): 50;
Elongation (≥%): 30;
Shape: Tube;
Est. Time(Days): 14;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: Nickel Alloy;
Alloy: Alloy;
Type: Nickel Alloy Tube;
Powder: Not Powder;
Wall Thickness: 0.3-3mm;
MOQ(Kg): 50;
Elongation (≥%): 30;
Shape: Tube;
Est. Time(Days): 14;
|