Specification |
CAS No.: 9002-86-2;
Formula: -Nhoco-CH2-2o-Conhch2-6nhco-;
EINECS: 618-449-1;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Yellow;
Fire Retardant: B2, B3;
Drum Color: Blue, Green;
Ratio: 1.1-1.7;
Raw Material: Polyurethane, Polyisocyanurate;
Foam Close: 92%;
Form: Liquid;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 95;
Density,g/cm3: 1.16-12;
Tensile Strength,MPa: 30-40;
Elongation at Break,%: 600;
Tack Free Time,Min: 5-15;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 43-50;
Density,g/cm3: 0.2-0.23;
Tensile Strength,MPa: 1.3;
Elongation at Break,%: 170;
Tear Strength,Kn/M: 15;
Rebounding,%: 58;
Compression Set(50% 6h, 45ºC),%: 10-15;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 82-95;
Density,g/cm3: 1.13-1.20;
100% Modulus,MPa: 4-12;
300% Modulus,MPa: 8-14;
Tensile Strength,MPa: 15-35;
Tear Strength,MPa: 75-132;
Elongation at Break,%: 400-700;
|
CAS No.: Not Applicable;
Formula: Not Applicable;
EINECS: Not Applicable;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Transparent;
Appearance: Transparent viscous liquid;
Color,(Fe/Co): 0;
Viscosity, cps. (@60ºC): 17000~35000;
Nco%: <0.1;
Oligomer, wt.%: 100;
Functionality: 2;
|