Specification |
Processing Object: Metal;
Molding Style: Forging;
Molding Technics: Pressure Casting;
Application: Agricultural Machinery Parts;
Material: Iron;
Heat Treatment: Tempering;
Surface Treatment: Electroplating;
Forging Tolerance: +/-0.1mm;
Standard: ASTM;
Forged Wheel: Port Crane Equipment;
Forging Crane Wheel: Port Container Crane Spare Part;
Trolley Wheel: Crane Equipment;
|
Processing Object: Metal;
Molding Style: Forging;
Molding Technics: Pressure Casting;
Application: Instrument Accessories;
Material: Steel;
Heat Treatment: Annealing;
Surface Treatment: Polishing;
Forging Tolerance: +/-0.2mm;
Standard: ASME;
Name: Forging Parts Carbon Steel Hot Forging Part;
Technology: Forging, Steel Forging Parts;
Brand Name: Xh;
Weight: 0.5-50kgs;
OEM and ODM: 100% with Drwings and Samples;
Testing: Magnetic Particle Inspector, CMM;
Machining: Tapping, Milling, Grinding etc;
Support Material: Iron Steel Aluminum Iron Ets;
Packaging: Wooden, Carton, Pallet;
Delivery Time: 15-30 Days;
|
Processing Object: Metal;
Molding Style: Forging;
Molding Technics: Cold Expending;
Application: Machinery Parts;
Material: Non-Magnatic Steel;
Heat Treatment: Soulution Treatment, Stress Reliving Treatment;
Surface Treatment: Machining;
Forging Tolerance: ±1;
Standard: GB,ASTM,DIN,En;
Dimension: 1243+3/1030-3*945+3;
Thickness: 106.5mm;
Weight: 2800kg;
Yield Strength: 1070-1210MPa;
Tensile Strength: ≥1070MPa;
Elongation: ≥15%;
Reduction in Area: ≥52%;
Impact: ≥75j;
Residual Stress: ≤90MPa;
Magnetic Conductivity: ≤1.05;
|
Processing Object: Metal;
Molding Style: Forging;
Molding Technics: Forging;
Application: Machinery Parts;
Material: Steel;
Heat Treatment: Quenching;
Surface Treatment: Polishing;
Forging Tolerance: +/-0.5mm;
Standard: AISI;
Material Grade of Forging Round Bars: AMS 6418;
Origin of Round Bars: China;
Size of Round Bars: 20mm-1000mm;
Melting Method of Round Bars: Vim+ESR;
Packing of Round Bars: Plywooden Case;
Heat Treatment of Round Bars: Hardening and Tempering;
|
Processing Object: Metal;
Molding Style: Forging;
Molding Technics: Cold Expending;
Application: Machinery Parts;
Material: Non-Magnatic Steel;
Heat Treatment: Soulution Treatment, Stress Reliving Treatment;
Surface Treatment: Machining;
Forging Tolerance: ±1;
Standard: GB,ASTM,DIN,En;
Dimension: 1196/990×810;
Thickness: 103mm;
Weight: 2248kg;
Yield Strength: 1000-1090MPa;
Tensile Strength: ≥1000MPa;
Elongation: ≥21%;
Reduction in Area: ≥60%;
Impact: ≥54j;
Residual Stress: ≤100MPa;
Magnetic Conductivity: ≤1.05;
|