| Specification |
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3, Fe2o3;
Shape: Roll;
Manufacturing Technique: Woven;
Kind: Ordinary Ceramic Fiber;
Reinforcement: Steel Wire or Glass Fiber;
Standard Length: 30 M;
Coating: Vermiculite;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Al2O3+Sio2: 96%;
Al2O3: 43%;
Size: 5-100mmx500X1000mm;
Certifiacte: ISO9001, CE, etc;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|