| Specification |
Usage: Capacitor;
Type: Metallized Film;
Material: Polyester;
Feather: Mositure Proof;
Hardness: Soft;
Transparency: Opaque;
Processing Type: Multiple Extrusion;
Thickness: 4um, 5um, 6um, 7um, 8um, 9um, 10um, 12um;
Inner Diameter: 75mm+1.0mm/-0.5mm;
Outer Diameter: 240 +10/-20mm. 320 +10/-40mm;
Widthness: According to Customer Requirement;
Free Margin: 2.5mm +/-0.4mm (or 2.0mm, 1.5mm);
Square Resistance: 7.5 +/- 25% (or 6-9 );
Heavy Edge Resistance: 2-4;
Storage: <=10 for 6 Months (From Delivery Date);
|
Type: Metallized Film;
Material: BOPP;
Hardness: Soft;
Transparency: Opaque;
Density: 0.905±0.005 G/Cm³;
Thickness: 2.2~15 μm;
Width: 45mm/50mm/62.5mm/75mm etc;
Margin: 2.0mm/2.5mm/4.0mm etc;
ID: 75mm;
Od: 175mm/220mm/280mm/320mm etc;
Tensile Strength: ≥100 (MPa);
Elongation at Break: 20~200 %;
Elastic Modulus: 2800(MPa);
Heat Shrinkage: ≤5% (120ºC, 10min);
Wetting Tension: 38 Mn/M (Corona Treated Side);
Melting Point: 172ºC;
Break-Down Voltage: ≥350 V/μm (23ºC, DC);
Margin Type: Single, Double, Multiple, Middle, Internal;
Lead Time: 7-20 Days After Payment Confirmed;
|
Type: Metallized Film;
Material: PET;
Hardness: Soft;
Transparency: Opaque;
Processing Type: Multiple Extrusion;
Density: 1.4 G/Cm³;
Thickness: 1.9μm ~ 12μm;
Width: 30mm/37.5mm/50mm/62.5mm etc;
Margin: 1.5/2.0/2.5/3.0/4.0/5.0 mm;
ID: 75mm;
Od: 180mm, 240mm, 300mm, 320mm, etc;
Tensile Strength: ≥84 (MPa);
Elongation at Break: ≥22%;
Elastic Modulus: 2800(MPa);
Heat Shrinkage: ≤2.5% ( 150°c, 10min);
Melting Point: 256ºC;
Break-Down Voltage: ≥200 ( 23°c,DC );
Margin Type: Single, Double, Multiple, Middle, Internal;
Lead Time: 7-20 Days After Payment Confirmed;
|
Type: Metallized Film;
Material: PET;
Hardness: Soft;
Transparency: Opaque;
Processing Type: Multiple Extrusion;
Density: 1.4 G/Cm³;
Thickness: 1.9μm ~ 12μm;
Width: 30mm/37.5mm/50mm/62.5mm etc;
Margin: 1.5/2.0/2.5/3.0/4.0/5.0 mm;
ID: 75mm;
Od: 180mm, 240mm, 300mm, 320mm, etc;
Tensile Strength: ≥84 (MPa);
Elongation at Break: ≥22%;
Elastic Modulus: 2800(MPa);
Heat Shrinkage: ≤2.5% ( 150°c, 10min);
Melting Point: 256ºC;
Break-Down Voltage: ≥200 ( 23°c,DC );
Margin Type: Single, Double, Multiple, Middle, Internal;
Lead Time: 7-20 Days After Payment Confirmed;
|
Type: Metallized Film;
Material: PET;
Hardness: Soft;
Transparency: Opaque;
Processing Type: Multiple Extrusion;
Density: 1.4 G/Cm³;
Thickness: 1.9μm ~ 12μm;
Width: 30mm/37.5mm/50mm/62.5mm etc;
Margin: 1.5/2.0/2.5/3.0/4.0/5.0 mm;
ID: 75mm;
Od: 180mm, 240mm, 300mm, 320mm, etc;
Tensile Strength: ≥84 (MPa);
Elongation at Break: ≥22%;
Elastic Modulus: 2800(MPa);
Heat Shrinkage: ≤2.5% ( 150°c, 10min);
Melting Point: 256ºC;
Break-Down Voltage: ≥200 ( 23°c,DC );
Margin Type: Single, Double, Multiple, Middle, Internal;
Lead Time: 7-20 Days After Payment Confirmed;
|