Specification |
CAS No.: Inv-V470;
Formula: Inv-V470;
EINECS: Inv-V470;
Molecular Principal Chain: Element Organic Polymer;
Color: Light Yellow Transparent Liquid;
Tensile Strength (MPa): 70;
Tensile Modulus (Gpa): 3.5;
Elongation at Break (%): 2.0-4.0;
Bending Strength (MPa): 140;
Flexural Modulus (Gpa): 3.5;
Impact Toughness (Kj/M2): 10.1;
Package Size Per Unit Product: 50.00cm * 100.00cm * 50.00cm;
Gross Weight Per Unit Product: 220.000kg;
|
CAS No.: 25135-73-3;
Formula: 0;
EINECS: 0;
Molecular Principal Chain: /;
Color: Transparent;
Viscosity(P/200ºC): 35_45;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 4-26;
300% Modulus,MPa: 8-28;
Tensile Strength,MPa: 30-50;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 4-26;
300% Modulus,MPa: 8-28;
Tensile Strength,MPa: 30-50;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|