Specification |
Fineness: Other;
Color: Natural Color;
Type: Blasting Media;
Moisture: 0.18%;
Refractive Index: 1.92-2.01;
Hardness(Mohs): 7-8;
Bulk Density(g/cm3)Tapplicationt,Melting: 4.6-4.7g/cm3;
Application: Refractory Materials, Fine Casting;
Melting Point: 2340-2550ºC;
Crystal State: Square Pyramidal Column;
Certificate: CE;
MOQ: 1ton;
|
Fineness: 0.25-0.6mm;
Color: Red;
Type: Natural Sand;
Shape: Sub-Conchoidal;
Chloride Content: 0.01%;
Specific Gravity: 4.1 g/cm3;
Business Type: Manufacturer;
Sample: Yes,We Can Supply Sample;
Mohs Hardness: 8.0 Mohs;
Certificate: SGS,Government Test Report;
Free Flow: 90% Minimum;
Payment Term: T/T,L/C;
Pathological Effects: None;
Average Bulk: 2.4 g/cm3;
Alumina: 16.60--18.10%;
Durability: Very Good;
Moisture Absorption: Non Hygroscopic, Inert.;
Magnetism: Very Slightly Magnetic;
|
Fineness: 0.25-0.6mm;
Color: Red;
Type: Natural Sand;
Shape: Sub-Conchoidal;
Specific Gravity: 4.1 g/cm3;
Mohs Hardness: 8.0 Mohs;
Durability: Very Good;
Certificate: SGS,Government Test Report;
Moisture Absorption: Non Hygroscopic, Inert.;
Free Flow: 90% Minimum;
Magnetism: Very Slightly Magnetic;
Payment Term: T/T,L/C;
Chloride Content: 0.01%;
Alumina: 16.60--18.10%;
Pathological Effects: None;
Average Bulk: 2.4 g/cm3;
Business Type: Manufacturer;
Sample: Yes,We Can Supply Sample;
|
Fineness: 0.18mm;
Color: Red;
Type: Natural Sand;
Garnet (Almandite): 97-98%;
Frcture: Sub-Conchoidal;
Al2O3: 16.72-18.06%;
Free Silica Content: None;
Specific Weight: 4.1g/cm3;
Average Bulk: 2.4G/Cm3;
Durability: Very Good;
Conductivity: Less Than 25 Micorsiemens Per Meter;
Standard: ISO;
Fe2 O3: 27.95-29.5%;
Certificate: SGS, Government Test Report;
Si O2: 37.44-37.77%;
MGO: 4.75%;
Cao: 9%;
Magnetism: Very Slightly Magnetic;
|
Fineness: 0.18mm;
Color: Red;
Type: Natural Sand;
Garnet (Almandite): 97-98%;
Frcture: Sub-Conchoidal;
Al2O3: 16.72-18.06%;
Free Silica Content: None;
Specific Weight: 4.1g/cm3;
Average Bulk: 2.4G/Cm3;
Durability: Very Good;
Conductivity: Less Than 25 Micorsiemens Per Meter;
Standard: ISO;
Fe2 O3: 27.95-29.5%;
Certificate: SGS, Government Test Report;
Si O2: 37.44-37.77%;
MGO: 4.75%;
Cao: 9%;
Magnetism: Very Slightly Magnetic;
|