Specification |
CAS No.: 25038-32-8;
Formula: C28h27n3o3HCl;
EINECS: 0;
Molecular Principal Chain: Carbon Chain Polymer;
Color: White;
Appearance: Transparent Pellets;
Usage: Plastic Modification;
Material: Styrene Isoprene Styrene Elastomer;
Raw Material: Synthetic Rubber;
Name: Styrene Isoprene Styrene Elastomer;
Grade: 1501;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|