Specification |
Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Motor, Insulating Varnish, Switch Baseplate;
Type: Insulation Tape;
Chemistry: Organic Insulation;
Material: Rubber;
Thermal Rating: 250 250;
Maximum Voltage: 20KV~100KV;
Classification: Hybrid Insulation Materials;
Color: Black;
Brand: Baijin;
Product Name: Wire Harness Wrapping Tape;
MOQ: Low;
Print: Support Multi-Color Printing;
Semi-Finished Products: Tape Jumbol Roll;
|
Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Motor, Insulating Varnish, Switch Baseplate;
Type: Insulation Sleeve;
Chemistry: Organic Insulation;
Material: PE;
Thermal Rating: B 130;
Maximum Voltage: <10KV;
Color: Black, Other Colors Can Be Customized;
Brand: Wellco;
Rated Voltage: 600V;
Shrink Ratio: 3:1 ( 4:1 Available);
Working Temperature: -40~125c;
Tensile Strength: 10.4MPa;
Feature: Flame Retardant, Flexible, Halogen Free;
|
Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Motor;
Type: Insulation Film;
Material: Polyimide;
Thermal Rating: 260;
Maximum Voltage: <10KV;
Color: Golden Color;
Thickness: 0.025mm/0.05mm/0.075mm/0.1mm/0.125mm/0.15mm/0.20mm;
Length: 1000m/2000m/3000m;
Elongation at Break: ≥ 50%;
|
Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Motor;
Type: Insulation Tape;
Chemistry: Hybrid Insulation;
Material: Silicone;
Thermal Rating: H 180;
Maximum Voltage: <10KV;
Classification: Hybrid Insulation Materials;
Color: White;
Thickness: 0.18mm;
Adhesion to Steel: 9 N/25mm;
Tensile Strength: 180 N /10mm;
Elongation at Break: 5%;
Temperature Resistance: 180 ºC;
Electrical Strength: 3kv;
Lenght: 30m;
|
Application: Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Motor, Electrical/Electronic Product;
Type: Insulation Film;
Material: Polyimide;
Thermal Rating: 260°;
Maximum Voltage: <10KV;
Color: Golden Color;
Thickness: 0.10mm;
Elongation at Break: ≥55%;
Tensile Strength Longitudinal Direction: ≥150MPa;
Length: 1000m/2000m/3000m;
Cross Direction: ≥130MPa;
Dielectric Strength: ≥200um;
Size Stability(150°): ≤0.35%;
Water Absorption: ≤4%;
|