Specification |
Application: Industrial Ceramic;
Type: Ceramic Plates;
Name: Aluminum Nitride Ceramic Heating Crucibles;
Size: Customized;
Shape: Customized;
Appearance: Neat;
Surface: Polished;
Property: Thermal Insulation;
Advantage: Long Working Life;
Usage: Electronic Products;
Feature: High Temperature Resistant;
Surface Roughness: Ra 0.2-0.6um;
Thermal Conductivity: >170W;
Flexural Strength(MPa): 382.7;
Dielectric Strength: 15 Kv/mm Min;
Key Word: Aluminum Nitride Ceramic Oil Cup;
Material: Aluminum Nitride Ceramic;
|
Application: Aerospace, Electronics, Medical, Refractory, Heatsink, Powe Module;
Type: Industrial Parts;
Volume Resistivity: ≥10(14);
Flexural Strength: ≥450MPa;
Color: Grey;
Dielectric Constant: 8-10 1MHz;
Thermal Conductivity: (25°c) 180 W/Mk;
Processing Service: Moulding;
Density: ≥3.33G/Cm3;
Feature: High Thermal Conductivity;
|
Application: Aerospace, for Grading or Bearings;
Type: Ceramic Plates;
Bulk Density: 3.25 g/cm3;
Maximum Use Temperature: 1000;
Flexural Strength: 880;
Elastic Modulus: 300;
Vickers Hardnes: 300;
Thermal Shock Resistance(20°c): 750;
Thermal Conductivity: 30 W/M.K;
Processing Service: Moulding;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Type: Silicon Nitride Ceramics;
Compressive Strength: 3000;
Maximum Use Temperature: 1500;
Advantage: Reduces Slag;
Color: Black, Gray;
Thermal Shock Resistance: 605-617;
Water Absorption: 0;
Density: 3.24-3.28;
|
Application: Aerospace, Electronics, Medical, Refractory, Structure Ceramic;
Type: Ceramic Rollers;
Flexural Strength (20ºC): 750-800 MPa;
Thermal Shock Resistance (20ºC): 22 W/M.K;
Vickers Hardness: 14;
Compressive Strength (20ºC): 3000 MPa;
Water Absorption: 0;
Processing Service: Moulding;
Density: 3.24 - 3.26;
Max Working Temperature: 1500ºC;
|