Specification |
CAS No.: 7085-85-0;
Formula: C6h7no2;
EINECS: 210-898-8;
Bonding Function: Floor Coating Epoxy Resin;
Morphology: Liquid Water Color;
Application: Automobile, Construction, Woodworking, Fiber & Garment, Packing, Fiberglass;
Material: Epoxy;
Classification: Thermosetting;
Main Agent Composition: Thermosetting Resin;
Characteristic: Waterproof;
Promoter Composition: Curing Agent;
Composition: Inorganic Material;
Color: Clear;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|