| Specification |
Casting Method: Thermal Gravity Casting;
Process: Lost Wax Casting;
Molding Technics: Gravity Casting;
Application: Auto Parts, Furniture Parts, Railway Parts;
Material: Stainless Steel, Carbon Steel, Aluminium Alloy;
Surface Preparation: Polishing, Electropolishing, Mirror Polishing, EL;
Surface Roughness: Ra 3.2-Ra12.5;
Machining Tolerance: +/-0.02mm or as Drawing Requirement;
Standard: DIN;
Make: as Your Drawing or Sample;
Machining: Tapping, Milling, Grinding, Drilling, CNC Machinin;
Weight: 0.05kg~150kg;
Max Manufacture Ability: 100 Ton Each Month;
Processing: Investment Casting;
|
Casting Method: Vacuum Casting;
Process: Lost Wax Casting;
Molding Technics: Precision Casting;
Application: Turbojet Engine;
Material: Superalloy Inconel713c;
Surface Preparation: Sand Blast;
Surface Roughness: Ra3.2;
Machining Tolerance: +/-0.01mm;
Standard: ASTM;
Tensile Test Temperature: Above 900 Degree;
Tensile Strength of High Temperature: Above 830MPa;
Elongation of High Temperature: Above 3%;
Persistent Creep Temperature at High Tem: Above 975 Degree;
Creep Tensile Strength at High Temperatu: Above 225MPa;
High Temperature Duration: Above 40h;
Test of Surface Defect: Fpt;
Test of Internal Defect: X-ray;
Test of Size: CMM;
|
Process: Lost Wax Casting;
Molding Technics: Pressure Casting;
Application: Vacuum Casting;
Surface Preparation: Sand Blast;
Surface Roughness: Ra3.2;
Machining Tolerance: +/-0.01mm;
Standard: ASTM;
Tensile Test Temperature: Above 900 Degree;
Tensile Strength of High Temperature: Above 830MPa;
Elongation of High Temperature: Above 3%;
Persistent Creep Temperature at High Tem: Above 975 Degree;
Creep Tensile Strength at High Temperatu: Above 225MPa;
High Temperature Duration: Above 40h;
Test of Surface Defect: Fpt;
Test of Internal Defect: X-ray;
Test of Size: CMM;
|
Casting Method: Vacuum Casting;
Process: Lost Wax Casting;
Molding Technics: Precision Casting;
Application: Turbojet Engine;
Material: Superalloy Inconel713c;
Surface Preparation: Sand Blast;
Surface Roughness: Ra3.2;
Machining Tolerance: +/-0.01mm;
Standard: ASTM;
Tensile Test Temperature: Above 900 Degree;
Tensile Strength of High Temperature: Above 830MPa;
Elongation of High Temperature: Above 3%;
Persistent Creep Temperature at High Tem: Above 975 Degree;
Creep Tensile Strength at High Temperatu: Above 225MPa;
High Temperature Duration: Above 40h;
Test of Surface Defect: Fpt;
Test of Internal Defect: X-ray;
Test of Size: CMM;
|
Casting Method: Thermal Gravity Casting;
Process: Investment Casting;
Molding Technics: Gravity Casting;
Application: Auto Parts;
Material: Stainless Steel;
Surface Preparation: Shot Blasting;
Surface Roughness: Ra1.6;
Machining Tolerance: +/-0.01mm;
Standard: DIN;
Packaging: Standard Packaging with Carton Box and Pallet;
Weight: 0.005-20kg;
|