| Specification |
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.25±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 4 N/mm^2;
Tensile Strength: ≥ 7 N/mm^2;
Elongation at Break: ≥ 250%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 10~20 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 4 mm/24hrs;
|
Bonding Function: Pressure sensitive Adhesive;
Morphology: Water Emulsion;
Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, BOPP Tape;
Material: Acrylic;
Classification: Pressure-Sensitive;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: White;
Polymer Type: Acrylic Copolymer;
Appearance: Pure White;
Holding Force: >=24 Hours;
Total Solid Content by Wt: 54.0%-56.0%;
pH Value at 25 Degrees Celsius: 6.1-9.0;
Viscosity(Mps/S): <=80;
Initial Adhesivion Force(GB): >=23#;
Coating Backer: BOPP, PVC, Pet Film, Paper, Masking Tape etc;
|
CAS No.: 63148-62-9;
Formula: C6h18osi2;
EINECS: C3h8n2o;
Bonding Function: Structural Adhesive;
Morphology: Solid-State;
Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Construction, Fiber & Garment, Footwear & Leather;
Material: Neoprene;
Classification: Hot Melt;
Main Agent Composition: Rubber;
Characteristic: Adhesives;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Yellow;
Brand Name: Magpow;
Mpd107: Contact Cement(305);
Appearance: Light Yellow Thick Liquid;
Solid Content(%): 16+-2;
Viscosity: 1500-2500(25 Centigrade, MPa.S);
Peel Strengthen(25 Centigrad*48h): More Than 40 (Canvas-Canvas N\2.5c);
Shelf Life: 12months;
Stock: Full;
Custom-Tailor: Can Accpet Customer's Brand and Design;
|
CAS No.: C3h8n2o;
Formula: C6h18osi2;
EINECS: C3h8n2o;
Bonding Function: Instant Adhesive;
Morphology: Thick Liquid;
Application: Construction, Fiber & Garment, Footwear & Leather;
Material: a:Epoxy Resin;B Sulfur Curing Agent;
Classification: Auto Parts and Hardware;
Main Agent Composition: Thermosetting Resin;
Characteristic: Double Components Glue;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: Light Blue or Red Thick Liquid;No Machine Impurity;
Brand Name: Magpow;
MPa109: Auto-Parts Glue;
Components Rate: a:B=1:1;
Applying Temperature: -30 to 100;
Curing Time(25centigrade,Min): Less Than 10;
Shear Strength: More Than 10MPa (Steel-Steel);
Stock: Full;
Custom-Tailor: Can Accept;
|
CAS No.: 68131-77-1;
Formula: /;
EINECS: /;
Bonding Function: High Temperature Resistant Adhesive;
Morphology: Solid-State;
Application: Packing, Coated Box Sealing;
Material: EVA;
Classification: Hot Melt;
Main Agent Composition: EVA;
Characteristic: High Viscosity;
Promoter Composition: Synthetic Resin;
Composition: EVA;
Color: Yellowish;
Shape: Granule;
Feature: Smokeless and Odorless;
Purpose: Box Sealing;
Packing: Bag Packing;
|