| Specification |
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.30±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~ 55 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Shore a Hardness: ~45;
Shear Strength: ≥ 1 N/mm^2;
Tensile Strength: ≥ 2 N/mm^2;
Elongation at Break: ~ 350%;
Tear Strength: 6 N/mm;
Origen: China;
Package: 310ml Cartucho 600ml Salchicha;
Uso: PARA Uso Interior;
|
Bonding Function: Spray Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Cloth Screen Glue;
Material: Polyester;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Yellow;
Solid Content: 35%;
Density: 0.80 Kg/L;
Viscosity: 40-70 Cps;
Shear Strength: 2.46 MPa;
Initial Strength: 0.7 MPa;
Tack Time: 2h;
|
CAS No.: 7085-85-0;
Formula: C6h7no2;
EINECS: 210-898-8;
Bonding Function: Hot-Melt or Normal Temperature Adhesive;
Morphology: Solvent;
Application: Footwear & Leather, Fiber & Garment, Packing, Shoe Making;
Material: Neoprene Bubber;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Yellow;
Solid Content: 19%-21%;
Viscosity(25degrees Celsius): 2000-3000cps;
Density: About 0.93kg/L;
Tack Time: Around 15 Minutes to 30 Minutes;
Appearance: Slight Yellow Semi-Translucent Viscous Liquid;
Main Component: Neoprene Rubber, Toluene, Butanone;
|
CAS No.: 95588-52-5;
Formula: Mixture;
EINECS: 95588-52-5;
Bonding Function: Hot-Melt or Normal Temperature Adhesive;
Morphology: Solvent;
Application: Footwear & Leather, Fiber & Garment, Packing, Shoe Making;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Yellow;
Solid Content: 22%-24%;
Viscosity(25degrees Celsius): 2000-4000cps;
Density: About 0.92 Kg/L;
Tack Time: Long (up to 60 Mins);
Appearance: Slight Yellow Viscous Liquid;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
|
Bonding Function: Spray Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Cloth Screen Glue;
Material: Polyester;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Yellow;
Solid Content: 35%;
Density: 0.80 Kg/L;
Viscosity: 40-70 Cps;
Shear Strength: 2.46 MPa;
Initial Strength: 0.7 MPa;
Tack Time: 2h;
|