Specification |
Material: PTFE;
Kind: White Plastic Sheet;
Tensile Strength: ≥25;
Apparent Density: 2.3±0.1g/cm3;
Ultimate Elongation: ≥200%;
Working Temp: -180 ~ 260°c;
Temperature: 385°c;
Melting Point: 327°c;
Hardness Rockwell: M65;
|
Material: NBR;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 1.5%~5.0%;
Tensile Strength: 81~130MPa;
Foam Type: NBR Foam;
Density: 60-90 Kg/M3;
Compression Set: <20%;
Elongation: >100%;
Thermal Conductivity: 0.038W/M*K;
Compression Deflection: 30-35kpa;
Foam Color: as Pantone Colors;
Thickness: 1-50mm;
Application: Construction, Industry;
Sample Foam: Available at Any Time;
|
Material: PE;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 3.46MPa;
Foam Type: Closed Cell PE Foam;
Density: 28-70kg/M3;
Hardness Shore C: 15-25;
Tensile: 160-450kpa;
Elongation: 180-250%;
Color: as Pantone Colors;
Foam Shape: Sheet or Roll;
Size: 1000X2000mm, 1500mm*2000mm;
Thickness: 5-50mm;
Application: Packing, Automobile, Construction..;
|
Material: PE;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 3.46MPa;
Foam Type: Closed Cell PE Foam;
Density: 28-70kg/M3;
Hardness Shore C: 15-25;
Tensile: 160-450kpa;
Elongation: 180-250%;
Color: as Pantone Colors;
Foam Shape: Sheet or Roll;
Size: 1000X2000mm, 1500mm*2000mm;
Thickness: 5-50mm;
Application: Packing, Automobile, Construction..;
|
Material: NBR, EPDM, Cr, EVA;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 3.46MPa;
Foam Type: NBR/PVC Foam;
Denstiy: 50-90kg/M3;
Tensile Rate: >120%;
Compression Deformation: <30%;
Tearing Strength: >2.5n/Cm;
Oxygen Index: >26%;
Foam Color: as Pantone Colors;
Thickness: 1-50mm;
Application: Construction, Industry;
Sample Foam: Avaliable at Any Time;
|