Specification |
Color: Black;
Name: Green Refractory Silicon Carbide;
Appearance: Black Partical/Bulk;
Sic: 98.5%or Above;
Place of Origin: Henan, China (Mainland);
Usage: Polishing/Grinding/Sandblasting/High-Grade Refract;
Abrasive Grain Sizes: 12-240#;
Delivery Time: Within 7 Days;
Grain Density: 3.95-3.97g/cm3;
Mohs Resistant: 9.56;
Refractoriness: Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Powder;
Material: Silicon Carbide (Sic);
Fe2o3: 0.03%;
|
After-sales Service: 7--24 Hour Online Service;
Color: Black;
Application: Refractory, Metallurgy, Chemical, Ceramic, Casting;
Chemical Composition: Si Fe Al Ca;
Material: Silicon Carbide;
Shape: Lump,Granule and Powder;
Usage: Casting Steelmaking;
Crystal Form: Polygon;
Mohs Hardness: 9.2-9.6;
Micro Hardness: 2840~3320kg/mm²;
Melting Point: 1723;
Maximum Operating Temperature: 1600;
True Density: 3.21g/Cm³;
Bulk Density: 2.30g/Cm³;
|
After-sales Service: 7--24 Hour Online Service;
Color: Black;
Application: Refractory, Metallurgy, Chemical, Ceramic, Casting;
Material: Silicon Carbide;
Specifications: 90%1-0mm;
Crystal Form: Polygon;
Shape: Lump,Granule and Powder;
Usage: Casting Steelmaking;
|
After-sales Service: Online;
Color: Green, Black;
Application: Refractory, Metallurgy, Chemical, Ceramic, Casting;
Shape: Powder;
Material: Silicon Carbide (Sic);
Refractoriness (Degree): Refractoriness (Degree);
Processing Service: Refractory, Abrasive;
Size: Customizable;
Usage: Polishing, Grinding, Sandblasting, Metallurgical;
Sample: Avaliable;
Sic Content: 98.5% Min;
Bulk Density: 1.45-1.56g/cm3;
Ture Density: 3.12 g/cm3;
|
After-sales Service: Online;
Color: Green, Black;
Application: Refractory, Metallurgy, Chemical, Ceramic, Casting;
Shape: Powder;
Material: Silicon Carbide (Sic);
Refractoriness (Degree): Refractoriness (Degree);
Processing Service: Refractory, Abrasive;
Size: Customizable;
Usage: Polishing, Grinding, Sandblasting, Metallurgical;
Sample: Avaliable;
Sic Content: 98.5% Min;
Bulk Density: 1.45-1.56g/cm3;
Ture Density: 3.12 g/cm3;
|