Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Cement;
Name: Red Fire Clay Brick;
Density (g/cm3): 2.05-2.75;
Standard Size (mm): 230*114*65mm;
Permanent Linear Change % 1500cx2h: -0.5%~+0.1%;
Refractoriness: 1740;
Cold Crushing Strength MPa: 20;
Apparent Porosity: 24%;
0.2 MPa Refractoriness Under: 1350c;
Color: Red Fire Brick;
Application: Fire Clay Brick for Industrial Furnaces;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Rectangle, etc;
Material: Alumina, Sic, Zirconia;
Size: 50*50*12mm,149.63/141.79*200*15,250*200*15mm,etc;
Porosity(%): 80-90;
Ppi: 10-60;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Plate;
Material: MGO Powder,Fiberglass Mesh Ect.;
Color: White, Grey, Red, Green;
Density: 0.96-1.12g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Plate;
Material: MGO Board;
Color: White, Grey, Red, Green;
Density: 0.96-1.12g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Color: White, Grey, Red, Green;
Density: 0.96-1.12g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|