Specification |
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Length: 1200/1000/900mm;
Width: 1000/600/500mm;
Thickiness: 5-100mm;
Ultimate Strength: 0.7MPa;
Chemical Composition: Al2O3+Sio2;
Thermal Conductivity: 0.085(400c)/0.132(800c);
Shrinkage (1800f, 3h: -3%;
Color: White;
Application: Liners of Industrial Furnace;
Product Name: Refractory Ceramic Fiber Board;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Filter Material, High Temperature Insulating Material, Industrial Ceramic;
Temprature Classification: 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Square, Hexagon, Circular, Triangle, etc.;
Kind: Industry Ceramic;
Bulk Density(Kg/M3): 500-680;
Middle Wall Thickness(mm): 0.3;
Thermal Expansion Coefficient(in/Ink): 1.5- 1.8;
Thermal Shock Resistance (K): Max 500;
Height(mm): 50;
Average Weight Per Piece(Kg): 0.3;
Specific Heat Capacity(J/Kgk): 850- 1000;
Water Absorption %: 20-25;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fibre Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|