Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >99.99%;
Alloy: Non-alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni200 Ni201;
MOQ: 1kg;
Surface: Bright;
Density: 8.908 G/Cm³;
Resistance: 0.096;
Melting Point: 1435-1446;
Treatment: Hydrogen Annealing;
Elongation: 35%;
Ultimate Strength: 462MPa;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Strip;
Powder: Not Powder;
Chemical Composition: Ni80cr20;
Product Name: Nichrome Foil;
Characteristics: High Resistivity, Good Oxidation Resistance;
The Highest Use Temperature: 1200c;
Density: 8.4G/Cm3;
Resisivity: 1.09uΩ/M;
Linear Expansion Coefficient: 18.0;
Elongation: >20%;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >99.95%;
Alloy: Alloy;
Type: Nickel Strip;
Powder: Not Powder;
Chemical Composition: Ni80cr20;
Product Name: Nichrome Foil / Strip;
Characteristics: High Resistivity, Good Oxidation Resistance;
The Highest Use Temperature: 1200c;
Density: 8.4G/Cm3;
Nichrome Strip Resisivity: 1.09+/-0.03;
Elongation: >20%;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Strip;
Powder: Not Powder;
Chemical Composition: Ni80cr20;
Product Name: Nichrome Foil;
Characteristics: High Resistivity, Good Oxidation Resistance;
The Highest Use Temperature: 1200c;
Density: 8.4G/Cm3;
Resisivity: 1.09uΩ/M;
Linear Expansion Coefficient: 18.0;
Elongation: >20%;
OEM: Yes;
Sample: Free;
Stock: Seyn;
Surface: Bright;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Strip;
Powder: Not Powder;
Chemical Composition: Ni80cr20;
Product Name: Nichrome Foil;
Characteristics: High Resistivity, Good Oxidation Resistance;
The Highest Use Temperature: 1200c;
Density: 8.4G/Cm3;
Resisivity: 1.09uΩ/M;
Linear Expansion Coefficient: 18.0;
Elongation: >20%;
|