Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: >98%;
Alloy: Alloy;
Type: Hastelloy Tube;
Powder: Not Powder;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Tensile Strength: 790;
Elongation: 40%;
Composition: Ni58%, Cr20%, Mo3.15%;
|
Application: Aviation, Electronics, Industrial, Medical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >99.95%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Sample: Free;
Delivery Time: 5-15days;
Name: Inconel 600 Wire;
Surface: Bright;
Criterion: ASTM Aws;
Diameter: 0.02-5.0mm;
OEM: Yes;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni80 % Cr20%;
Product Name: Nichrome Wire;
Characteristics: High Resistivity, Good Oxidation Resistance;
The Highest Use Temperature: 1200c;
Density: 8.4G/Cm3;
Resisivity: 1.09;
Elongation: >20%;
Sample: Free;
Serves: Small Order Accepted;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni 76%;
Characteristics: High Resistivity, Good Anti-Oxidation Resistance;
Range of Application: Resistor, Heater,Chemical;
Electrical Resistivity: 1.09 Ohm mm2/M;
The Highest Use Temperature: 1400;
Density: 8.4G/Cm3;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1200;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni 76%;
Characteristics: High Resistivity, Good Anti-Oxidation Resistance;
Range of Application: Resistor, Heater,Chemical;
Electrical Resistivity: 1.09 Ohm mm2/M;
The Highest Use Temperature: 1400;
Density: 8.4G/Cm3;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1200;
|