Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 44%;
Alloy: Alloy;
Type: CuNi Wire;
Powder: Not Powder;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Max Working Tem: 250c;
Resistivity: 0.15ohm/M;
Density: 8.9g/cm3;
TCR X10-6 / 0c (20~600 0c): <50;
Emf Vs Cu (μV/ 0c) (0~100 0c): -25;
Melting Point: 1100c;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.62;
Density: 8.5 Cm3;
Curie Point: 330 C;
Name: Ni80cr3;
Hardness: 130~240 Hv;
Tensile Strength: 560~930 MPa;
Yield Strength: 150~885 MPa;
Elongation: 4~40 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.56;
Density: 8.75 Cm3;
Curie Point: 400 C;
Name: Ni80mo4;
Hardness: 130~240 Hv;
Tensile Strength: 560~930 MPa;
Yield Strength: 150~885 MPa;
Elongation: 4~40 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.56;
Density: 8.75 Cm3;
Curie Point: 400 C;
Name: Ni80mo4;
Hardness: 130~240 Hv;
Tensile Strength: 560~930 MPa;
Yield Strength: 150~885 MPa;
Elongation: 4~40 %;
Use: High Frequency Inductive Components;
|